無塵室無粉乳膠手指套

無粉靜電消散乳膠手指套

(Rohs ready)

100%天然乳膠製造

  • Width (mm):S25 / M27 / L29

  • Length (mm):

Roll: S66 ± 3 / M68 ± 3 / L 68 ± 3

  • Physical Test (ASTM D412)

Elongation:Min. 700%

Tensile Strength:Min. 25 Mpa

  • Average Surface Resistivity :

(ASTM D257)表面阻抗

106 ~ 109 Ohm/square

粉紅無粉防靜電乳膠手指套 (Rohs ready)

Suzuki Latex 100%天然乳膠製造

  • Internal diameter (mm):

S15 / M16.5 & 18 / L21

  • Thickness (mm):0.1 ± 0.02

  • Length (mm):

Unroll:63 ± 2/Roll:63 ± 2

  • Physical Test (ASTM D412)

Elongation:Min. 700%

Tensile Strength:Min. 25 Mpa

  • Average Surface Resistivity

(ASTM D257)表面阻抗

1010 ~ 1012 Ohm/square

黑色無粉靜電消散乳膠手指套 (Rohs ready)

Suzuki Latex 100%天然乳膠製造

  • Internal diameter (mm):

S15 / M16.5 & 18 / L21

  • Thickness (mm):0.1 ± 0.02

  • Length (mm):

Unroll:63 ± 2 / Roll:63 ± 2

  • Physical Test (ASTM D412)

Elongation:Min. 700%

Tensile Strength:Min. 25 Mpa

  • Average Surface Resistivity (

ASTM D257)表面阻抗

109 Ohm/square

無粉防靜電Nitirle手指套

(Rohs ready)

Suzuki Latex 100%人造橡膠製造

  • Internal diameter (mm):

S15 / M16.5 & 18

  • Thickness (mm):0.11 ± 0.02

  • Length (mm):

Unroll:60 ± 3 / Roll:60 ± 3

  • Physical Test (ASTM D412)

Elongation:Min. 700%

Tensile Strength:Min. 25 Mpa

  • Average Surface Resistivity (

ASTM D257)表面阻抗

1010 ~ 1011 Ohm/square

應用:乳膠手指套可替代乳膠手套,產線人員可戴在防靜電手套外,節省成本

產業:電子產業,組裝業,精密機械,光學產業

注意事項:

    1. 請放置室內通風處,室溫低於28ºC

    2. 避免直接接觸陽光

    3. 打開包裝後請盡快使用

  • 乳膠手指套：天然橡膠製成，可防護細菌、病毒

  • NBR手指套：由合成橡膠製成，可防護化學品、病毒

1.材質:

  • 乳膠手指套：天然橡膠製成，取自於橡膠樹汁液，天然乳膠是一種生物合成產品

  • NBR手指套：是一種橡膠，主要由丙烯腈和丁二烯合成

2.防過敏性:

  • 乳膠手指套：含蛋白質，對於易過敏體質的人，容易產生過敏反應。

  • NBR手指套：不含蛋白質、氨基化合物及其他有害物質，極少產生過敏。

3.可降解性:

  • 乳膠手指套：可 / NBR手指套：可

4.彈性:

  • 乳膠手指套 > NBR手指套

5.防刺穿性:

  • NBR手指套> 乳膠手指套

6.價格:高-->低

  • NBR手指套> 乳膠手指套

以上資料僅供客戶參考,可依貴司需求自行選購